PPS-Excellent chemical resistance
PPS-tight tolerance
PPS-better thermal performance
PPS-dimensional stable flame retardant
|
Property |
Test Method |
Units |
Fiberglass Reinforced |
|||||
|
P130T |
P130T-04 |
P140T |
P140T-02 |
P140T-04 |
||||
|
Physical |
Density |
ISO 1183 |
g/cm3 |
1.56 |
1.56 |
1.65 |
1.65 |
1.65 |
|
Water Absorption |
ISO 62 |
% |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
|
|
MD/TD* |
- |
% |
0.4/0.7 |
0.4/0.7 |
0.3/0.6 |
0.3/0.6 |
0.3/0.6 |
|
|
Mechanical |
Tensile Strength |
ISO 527 |
MPa |
150 |
145 |
185 |
180 |
175 |
|
Elongation at Break |
ISO 527 |
% |
3.0 |
6.0 |
2.0 |
4.0 |
4.0 |
|
|
Flexural Strength |
ISO 178 |
MPa |
220 |
210 |
260 |
250 |
250 |
|
|
Flexural Modulus |
ISO 178 |
GPa |
11.0 |
8.0 |
13.0 |
12.0 |
11.5 |
|
|
Impact Strength |
ISO 180 |
kJ/m2 |
10.0 |
12.0 |
12.0 |
14.0 |
15.0 |
|
|
Rockwell Hardness |
ISO 2039/2 |
R scale |
120 |
120 |
120 |
120 |
120 |
|
|
Thermal |
Heat Deflection Temperature |
ISO 75 |
°C |
265 |
265 |
265 |
265 |
265 |
|
Flammability Rating |
UL-94 |
- |
V0 |
V0 |
V0 |
V0 |
V0 |
|
|
Electrical |
Volume Resistivity |
ISO 167 |
Ohm.cm |
5×1016 |
5×1016 |
5×1016 |
5×1016 |
5×1016 |
|
Dielectric Strength |
ASTM D149 |
KV/mm |
16 |
16 |
16 |
16 |
16 |
|
|
Dielectric Constant |
ASTM D150 |
- |
3.6 |
3.6 |
3.8 |
3.8 |
3.8 |
|
|
Wastage Factor |
ASTM D150 |
- |
0.002 |
0.002 |
0.002 |
0.002 |
0.002 |
|
|
Process Conditions |
Injection Temperature |
- |
°C |
290~330 |
290~330 |
290~330 |
290~330 |
290~330 |
|
Mold Temperature |
- |
°C |
120~150 |
120~150 |
120~150 |
120~150 |
120~150 |
|
|
* MD: Mold direction; TD: Transverse direction |
||||||||