Click image to view original picture
Fire Clay Brick
1.Good volumn stability
2.Excellent Corrosion and abrasion Resistance
3.Good thermal shock resistace
Feature:
1.bricks are made from high quality bauxite
2.dry pressed
3.burned under tunnel kiln
4.accurate dimension
5.high strength
Product specification: standard form, normal standard, shaped and special shaped bricks.Can be used in various kilns because of its cheapness and general tray package. Among all of the refractory materials, it is the mostly used in the key positions.Molding method: it has down draft kiln and tunnel kiln and the general sintering temperature is 1360-1480 degrees. It is a kind of aluminosilicate refractory product which aluminum oxide (Al2O3) content is higher than 48%.
|
Fire clay brick SK-32 |
|
|
Item |
Standard |
|
AI2O3(%) |
30 |
|
Fe2O3 (%) |
3 |
|
Refractoriness (SK) |
32 |
|
Refractoriness under load, 0.2MPa, Ta, ((°C) |
1300 |
|
Porosity (%) |
22-26 |
|
Bulk density (g/cm³) |
2.05 |
|
Cold crushing strength (MPa) |
25 |
|
Thermal expansion at 1000°C (%) |
0.6 |
|
Fire clay brick SK-34 |
|
|
Item |
Standard |
|
AI2O3(%) |
38 |
|
Fe2O3 (%) |
2.5 |
|
Refractoriness (SK) |
34 |
|
Refractoriness under load, 0.2MPa, Ta, ((°C) |
1350 |
|
Porosity (% |
19-23 |
|
Bulk density (g/cm³) |
2.10-2.15 |
|
Cold crushing strength (MPa) |
25 |
|
Thermal expansion at 1000°C (%) |
0.6 |
|
Fire clay brick SK-36 |
|
|
Item |
Standard |
|
AI2O3(%) |
50 |
|
Fe2O3 (%) |
2 |
|
Refractoriness (SK) |
36 |
|
Refractoriness under load, 0.2MPa, Ta, ((°C) |
1450 |
|
Porosity (% |
20-24 |
|
Bulk density (g/cm³) |
2.30-2.40 |
|
Cold crushing strength (MPa) |
45 |
|
Thermal expansion at 1000°C (%) |
0.3 |