modified PA engineering plastics polyamide polymer nylon granules
with GF High-temp. resistant
flame-retardant
modified PA engineering plastics polyamide polymer nylon granules
we are a factory which mainly produces flame-redundant nylon series products which are anti-high-temperature, environment-friendly, and of high strength and technology content. they are now widely used in various newly-emerging fields, including automobile, communication, electronics, electrical appliance, household appliance and sports products etc.
|
Performance |
Test condition |
Testing standard |
Units |
TW80F6 |
|
|
Mechanical property |
|||||
|
Tensile modulus |
50mm/min |
ISO527-1/2 |
Mpa |
1980 |
|
|
Yield stress |
50mm/min |
ISO527-1/2 |
Mpa |
45 |
|
|
Tensile strength |
50mm/min |
ISO527-1/2 |
Mpa |
145 |
|
|
Elongation at break |
5mm/min |
ISO527-1/2 |
% |
1.6 |
|
|
Bending modulus |
2mm/min |
ISO178 |
Mpa |
9800 |
|
|
Bending strength |
2mm/min |
ISO178 |
Mpa |
235 |
|
|
Charpy notched impact strength |
23°C |
ISO179/leA |
KJ/m2 |
8 |
|
|
Charpy unnotched impact strength |
23°C |
ISO179/leA |
KJ/m2 |
40 |
|
|
Thermal |
|||||
|
Melting |
DSC.10K/min |
ISO3146 |
°C |
305 |
|
|
Heat distortion temp. A |
1.8Mpa |
ISO75 |
°C |
268 |
|
|
Heat distortion temp. B |
0.45Mpa |
ISO75 |
°C |
282 |
|
|
Electrical property |
|||||
|
Surface resistivity |
IEC60093 |
Ohm |
1/0.1 |
||
|
Volume resistivity |
IEC60093 |
Ohm×cm |
10/0.1 |
||
|
Anti-arc-track of |
TestotutionA |
IEC60012 |
V |
||
|
Physical property |
|||||
|
Density |
23°C |
ISO1183 |
g/cm3 |
2 |
|
|
Hygroscopicity |
23°C,50%r.h |
ISO62 |
% |
||
|
Absorbent/water absorption |
23°C |
ISO62 |
% |
0.35 |
|
|
Radial shrinkage |
flow |
ISO294-4 |
% |
0.3 |
|
|
Transverse shrinkage |
transverse |
ISO294-4 |
% |
0.7 |
|
|
Flame retardant |
|||||
|
Flammability test |
1.6/3.0mm |
UL94 |
V-0 |
||
|
The level of flame-retardant test |
1mm thickness |
ISO3795 |
mm/min |
||
|
Material de |
30%GF High-temp. resistant & flame retardant PA |
||||