Click image to view original picture
1)Flame retardant
2)Low volatility
3)non-corrosion property to metals
4)Low odor cure; releases an alcohol vapor during cure
Provides the following component flame retardant rtv silicon rubbercharacteristics:
|
Technology |
Silicone |
|
Chemical type |
White viscous paste |
|
Appearance (uncured) |
Translucent liquid |
|
Components |
One component - requires no mixing |
|
Cure |
Room temperature vulcanizing (RTV) |
|
Specific benefit |
Flame retardant |
|
Applications |
Sealing and gluing |
TIPICAL PRODUCT DATA
|
TYPICAL UNCURES PROPERTIES |
||
|
Appearance |
White viscous paste |
|
|
PH |
7.2 |
|
|
Tack-free time(23°C) |
min |
3 |
|
TYPICAL CURED PROPERTIES (7DAYS @ 23°C /50% RH) |
||
|
Appearance |
Elastic rubber |
|
|
Specific gravity |
1.45 |
|
|
Hardness |
Type A |
70 |
|
Tensile strength |
MPa |
2.58 |
|
Breaking elongation |
% |
88 |
|
Shear bond strength |
MPa |
2.5 |
|
Volatile siloxane |
Wt % |
0.028 |
|
Dielectric strength |
KV/mm |
20 |
|
Volume resistivity |
M •m |
2*107 |
|
Dielectric constant(50Hz) |
3.8 |
|
|
Dielectric loss(50Hz) |
0.005 |
|
GENERAL INSTRUCTIONS AND PRECAUTIONS
Avoid getting uncured material in the eyes, take eye protection at all times when working with this product.
Extended contact with the skin can cause irritation and should be avoided.
Wear protective gloves when working with this product.
Maintain good ventilation in the workplace at all times
DIRECTIONS FOR USE
For best performance bond surfaces should be clean and free from grease.
Full performance properties will develop over 72 hours.
Moisture curing begins immediately after the product is exposed to the atmosphere, therefore parts to be assembled should be mated within a few minutes after the product is dispensed.
Excess material can be easily wiped away with non-polar solvents
STORAGE
Store in a dry, cool place away from direct sunlight Optimal Storage: 8°C to 21°C. Storage below 8°C or greater than 28°C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container.
Note
The data contained herein are furnished for information only and are believed to be reliable. We cannot assume responsibility for the results obtained by others over whose methods we have no control. It is the user's responsibility to determine suitability for the user's purpose of any production methods mentioned herein and to adopt such precautions as may be advisable for the protection of property and of persons against any hazards that may be involved in the handling and use thereof. We recommend that each prospective user test his proposed application before repetitive use, using this data as a guide.